Composition: Al2O3
Application:Glass Kiln, incinerator
ZrO2:15-65%
Main Raw Material:Zircon sand and mullite or corundum
Size:As your requirements
Max Working Temperature:At least 1650℃
Product Introduction
Zircon bricks are made of zirconia and zirconia corundum cement as raw materials, mixed with rubber, molded, dried, and fired in a shuttle kiln at high temperatures.
Features
1.High molecular structure density.
2.High bulk density.
3.Good thermal shock stability.
4.Alkali and corrosion resistance.
Application
Zircon bricks are mainly used in alkali glass, borosilicate glass pool kiln bottom, upper space brick, brick hook, gap brick, flow slot brick, thermocouple brick and observation hole brick and other parts.
Technical Data
Item | ZS-G | ZS-Z | ZS-65A | ZS-65B | ZS-63 |
ZrO2(%) | >=65 | >=68 | >=65 | >=65 | >=63 |
SiO2(%) | <=33 | <=30 | <=33 | <=33 | <=35 |
Fe2O3(%) | >=0.2 | >=0.2 | >=0.2 | >=0.2 | >=0.2 |
TiO2(%) | <=1.2 | <=1.2 | <=1.2 | <=1.2 | -- |
Apparent Porosity(%) | <=10 | <=11 | <=17 | <=19 | <=20 |
Bulk Density( g/cm3) | >=4.30 | >=4.10 | >=3.70 | >=3.60 | >=3.55 |
Cold Crushing Strength(Mpa) | >=300 | >=200 | >=100 | >=80 | >=60 |
Refractoriness Under Load ( 0.2MPa,0.6%) (℃) | >=1700 | >=1700 | >=1680 | >=1650 | >=1600 |